INCAZELO YOMKHIQIZO
I-SZUV-S9006 iyi-ABS efana ne-SL resin enakhoukuqina okuphezuluizici. Idizayinelwe amaphrinta we-SLA wesifunda esiqinile. I-SZUV-S9006 ingasetshenziswa kumaphethini ayinhloko, amamodeli womqondo, izingxenye zomhlangano kanye nama-prototypes asebenzayo emkhakheni wezimboni zezimoto, zezokwelapha kanye nezabathengi. Izingxenye zokwakha eziqinile nge-SZUV-S9006 zingaphezu kwezinyanga ezingu-6.5.
?
OKUJWAYELEKILEIZICI
-I-liquid resin's viscosity ephakathi, ukunameka kalula, ukuhlanza izingxenye nemishini kulula
-Amandla athuthukisiwe agciniwe, ukugcinwa kobukhulu obuthuthukisiwe kwezingxenye ezisesimweni somswakama
-Udinga ingxenye encane yokuqedela
-Impilo yeshelufu ende emshinini
-Phansiukufinyela phansi?
?
OKUJWAYELEKILEIZINZUZO
-Udinga isikhathi esincane sokuqeda, kulula ukuphulukiswa
-Bulid izingxenye ezinembile neziphakeme eziqinile ezinokuqina okuthuthukisiwe kwe-dimensional
- Izilawuli zekhwalithi ephezulu zezingxenye zokuphonsa i-vacuum
-Ukushwabana okuphansi nokumelana kahle nokubaphuzi
-Magnificent umbala omhlophe
-Izinto ezibonakalayo ze-SLA eziphuma phambili?
Qaphela: izinga lokushisa le-szuv-s9006 akufanele libe phezulu kakhulu. Sicela uyisebenzise ngaphansi kuka-25℃. Umswakama ohlobene wokusetshenziswa nokugcinwa kufanele ube ngaphansi kuka-38RH%.
?
Amacala ohlelo
AMANYE AMAPROJEKTHI AMI
Imfundo
Izibungu Ezandla
Izingxenye ze-Auto
Idizayini yokupakisha
I-Art Design
Ezokwelapha
?
?Izakhiwo Zomzimba (Uketshezi)
| Ukubukeka | Emhlophe |
| Ukuminyana | 1.11-~1.15g/cm3@25 ℃ |
| I-Viscosity | 230~290cps @ 26 ℃ |
| Dp | 0.13~0.145 mm |
| Ec | 9.5~10.5 mJ/cm2 |
| Ugqinsi lwesendlalelo sokwakha | 0.05~0.12mm |
?
Izakhiwo Zemishini (Post-Cured)
| ISILINGANISO? | INDLELA YOKUHLOLA? | VALUE |
| Imizuzu engama-90 yokwelapha ngemuva kwe-UV | ||
| Ukuqina, Shore D | I-ASTM D 2240 | 75-85 |
| Flexural modulus, Mpa | I-ASTM D790 | 2,592-2,675 |
| Amandla e-Flexural, Mpa | I-ASTM D790 | 63-70 |
| I-tensile modulus, i-MPa | I-ASTM D638 | 2,489-2,595 |
| Amandla aqinile, i-MPa | I-ASTM D638 | 36-53 |
| Ukwandisa ngesikhathi sekhefu | I-ASTM D638 | 15-25% |
| Isilinganiso sikaPoisson | I-ASTM D638 | 0.4-0.44 |
| Amandla omthelela anophawu lwe-Izod, J/m | I-ASTM D 256 | 45-70 |
| Izinga lokushisa lokuphambuka kokushisa, ℃ | I-ASTM D 648 @66PSI | 38-50 |
| Ukuguqulwa kwengilazi,Tg | I-DMA, E”peak | 40-54 |
| I-coefficient ye-thermal expension | I-TMA(T | 90~102*E-6 |
| Ukuminyana, g/cm3 | ? | 1.12-1.18 |
| I-Dielectric Constant60 Hz | I-ASTM D 150-98 | 4.2-5.0 |
| I-Dielectric Constant 1 kHz | I-ASTM D 150-98 | 3.3-4.2 |
| I-Dielectric Constant1 MHz | I-ASTM D 150-98 | 3.2-4.0 |
| I-Dielectric StrengthkV/mm | I-ASTM D 1549-97a | 12.8-16.1 |
?